Stainless Steel 430 Bolts
Stainless Steel 430 Fasteners are made up of a 16% chromium, carbon, manganese, silicon, phosphorus and sulfur containing martensitic stainless steel. The material has 310MPa minimum yield strength and 483MPa minimum tensile strength. There are different types of fasteners in this grade such as the SS UNS S43000 Hex Head Bolts, square nuts, stud bolts, socket anchor bolts, eye bolts lag nuts, washers, pan head screws and many other types.
Stainless Steel 430 Bolts
SS 430 Hex Bolt
ASTM A193 SS Stud Bolts
The material has 183HB max Brinell hardness and 22% elongation rate. The SS 430 Bolt comes under the ASTM A193 specification. The dimensions vary according to the ASME B19.2.1, DIN 931, ASME Ba8.3 and other international standards. The size of the different types of the 430 Stainless Steel Bolt can range from M02 to M33 with lengths ranging from 3mm to 200mm. The threaded fasteners have different types of threads according to the thread configurations such as the ASME B1.1 2A/3A and so on. The ASTM A193 430 Stainless Steel Hex Bolt is one of the most commonly used fasteners as it is easily driven with hex tools. The removing the hex nuts is also easy with a tool. There are special types of fasteners such as the Stainless Steel 430 Eye Nuts which are used with heavy load bearing applications. The material is a high wear and tear resistant material. Therefore the fasteners are used in transportation, outdoor, furniture, paneling and other wear and tear applications.
Table of Content
- Most Frequent Types Of Stainless Steel 430 Fasteners
- Specification of Grade 430 Stud Bolt
- Size Chart UNS S43000 Threaded Rod
- Dimensions of DIN 1.4016 aisi 430 Nuts
- 430 Stainless Steel Bolts Chemical Composition Table
- Mechanical Properties of Grade 430 machine screw
- DIN 1.4016 stainless steel hex head bolt Equivalent Material
SS 430 Heavy Hex Bolts
430 SS Lag Bolts
SS 430 Anchor Bolts
SA193 SS 430 Hex Bolts
430 SS Double Ended Studs
430 SS Threaded Rod
AISI 430 Acorn Nuts
SS UNS S43000 T Nuts
430 SS Hex Head Nuts
A193 SS UNS S43000 Hex Nuts
Stainless Steel UNS S43000 Ogee Washers
SUS430 Stainless Steel Flat Washers
Material |
Specification |
Standards | Length |
Size |
430 Stainless Steel Fasteners
|
IS BS ASTM |
DIN, ISO, JIS, GB, IS, BS, ASTM | 3 mm to 200 mm |
M 02 to M 160 |
Nut Size (mm) |
Diameter* (mm) |
Height (mm) |
||
|---|---|---|---|---|
Hex Nut |
Jam Nut |
Nylock Nut |
||
2 |
4 |
1.6 |
1.2 |
- |
2.5 |
5 |
2 |
1.6 |
- |
3 |
5.5 |
2.4 |
1.8 |
4 |
4 |
7 |
3.2 |
2.2 |
5 |
5 |
8 |
4 |
2.7 |
5 |
6 |
10 |
5 |
3.2 |
6 |
7 |
11 |
5.5 |
3.5 |
- |
8 |
13 |
6.5 |
4 |
8 |
10 |
17 |
8 |
5 |
10 |
12 |
19 |
10 |
6 |
12 |
14 |
22 |
11 |
7 |
14 |
16 |
24 |
13 |
8 |
16 |
18 |
27 |
15 |
9 |
18.5 |
20 |
30 |
16 |
10 |
20 |
* This is the diameter across the flats. It is also the size of wrench to use. |
||||
NOMINAL SIZE (D) |
BODY DIAMETER |
HEAD THICKNEASTM A193 |
ACROASTM A193 THE FLATS |
ACROASTM A193 CORNERS |
||||
|---|---|---|---|---|---|---|---|---|
D (MAX) |
D (MIN) |
H (MAX) |
H (MIN) |
F (MAX) |
F (MIN) |
C (MAX) |
C (MIN) |
|
m10 |
10.00 |
9.78 |
6.63 |
6.17 |
17.00 |
15.73 |
18.48 |
17.77 |
m12 |
12.00 |
11.73 |
7.76 |
4.24 |
19.00 |
17.73 |
20.78 |
20.03 |
m14 |
14.00 |
13.73 |
9.09 |
8.51 |
22.00 |
20.67 |
24.25 |
23.35 |
m16 |
16.00 |
15.73 |
10.32 |
9.68 |
24.00 |
23.67 |
27.71 |
26.75 |
m20 |
20.00 |
19.67 |
12.88 |
12.12 |
30.00 |
29.16 |
34.64 |
32.95 |
m24 |
24.00 |
23.67 |
15.44 |
14.56 |
36.00 |
35.00 |
41.57 |
39.55 |
m30 |
30.00 |
29.67 |
19.48 |
17.92 |
46.00 |
45.00 |
53.12 |
50.85 |
m36 |
36.00 |
35.61 |
23.38 |
21.63 |
55.00 |
53.80 |
63.51 |
60.79 |
m42 |
42.00 |
41.38 |
26.97 |
25.03 |
65.00 |
62.90 |
75.06 |
71.71 |
m48 |
48.00 |
47.38 |
31.07 |
28.93 |
75.00 |
72.60 |
86.60 |
82.76 |
m56 |
56.00 |
55.26 |
36.2 |
33.80 |
85.00 |
82.20 |
98.15 |
93.71 |
m64 |
64.00 |
63.26 |
41.32 |
38.68 |
95.00 |
91.80 |
109.70 |
104.65 |
m72 |
72.00 |
71.26 |
46.45 |
43.55 |
105.00 |
101.40 |
121.24 |
115.60 |
m80 |
80.00 |
79.26 |
51.58 |
48.42 |
115.00 |
111.00 |
132.72 |
126.54 |
m90 |
90.00 |
89.13 |
57.74 |
54.26 |
130.00 |
125.50 |
150.11 |
143.07 |
m100 |
90.00 |
99.13 |
63.9 |
60.10 |
145.00 |
140.00 |
167.43 |
159.60 |
| Component | Wt. % |
| C | Max 0.12 |
| Cr | 16 – 18 |
| Fe | Min 79.31 |
| Mn | Max 1 |
| Ni | Max 0.5 |
| P | Max 0.04 |
| S | Max 0.03 |
| Si | Max 1 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell B | 85 | 85 | |
| Tensile Strength, Ultimate | 483 MPa | 70100 psi | |
| Tensile Strength, Yield | 310 MPa | 45000 psi | 0.2% YS |
| Elongation at Break | 25 % | 25 % | in 2 inches |
| Modulus of Elasticity | 200 GPa | 29000 ksi |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of thermal Expansion (m/m/0C) | thermal Conductivity (W/m.K) | Specific Heat 0-1000C (J/kg.K) | Electrical Resistivity (n.m) | |||
|---|---|---|---|---|---|---|---|---|---|
| 0-1000C | 0-3150C | 0-5380C | at 1000C | at 5000C | |||||
| 430 | 7750 | 200 | 10.4 | 11.0 | 11.4 | 26.1 | 26.3 | 460 | 625 |