ASTM F593 Bolts
Manufacturer of ASME SF593G Threaded Rod in India, With Affordable Price
The ASTM F593 Nut Bolt in group1 can be made up of the 303, 304, 305, 384 austenitic stainless steels. The 316 austenitic stainless fasteners belong to the alloy group 2 and 321 347 grades belong to the alloy group 3. The ASTM F593 18-8 Stud can be made of ferritic alloys in group 4, martensitic alloys of groups 5 and 6 with precipitation hardening alloys of group 7.
ASTM F593 Bolts Manufacturer in India, fasteners are designed with different strength ratings that come with various material grade. These chemical include carbon, manganese, phosphorus, sulfur silicon and chromium within the materials being used. The minimum tensile strength varied between 65ksi to 150 ksi while the minimum yield strength ranged between 20ksi to 65ksi.
The hardness of the ASTM F593 cw Nuts ranges up to B95. Companies such as Regal Sales Corporation supplies the different types of fasteners in this range for instance the ASTM F593 Screws and studs. You are welcome to contact us for further details and cost more specifically on the various classifications of fasteners mentioned in this specification.
ASTM F593 Fasteners
ASTM F593 Screw
ASTM F593 Nut Bolt
Table of Content
- What is ASTM F593 Bolts?
- Specifications of ASTM F593 Bolts
- Types of ASTM F593 Bolts
- F593 Hex Bolt Standard Dimensions Chart
- ASME SF593 Heavy Hex Bolts Size Chart
- ASME SF593 Hex Bolt Torque Chart
- ASTM F593 Hex Head Bolt Physical Properties
- Chemical Composition of ASTM F593 Washer
- F593C Hex Head Bolt Weight Chart
- Equivalent Material Grade of ASTM F593 Nut Bolt
- Mechanical Properties of ASTM F593 Bolts
- Delivery Time Table of ASTM F593 Anchor Bolt
- What is the Difference Between ASTM F593 and ASTM A193 Bolts?
- How Do ASTM F593 Bolts Perform in Extreme Temperatures?
- Can ASTM F593 Bolts Be Welded?
ASTM F593 Bolts range from ¼ inches to 1 ½ inches in diameter. The specification covers stainless steel bolts, studs and cap screws in this diameter range. ASTM F593 Bolts Manufacturer in India, There are different materials used to produce these fasteners. There are 8 groups of alloys that are used and based on the group the material grade differs.
Find Grade F593 Flange Head Bolt & ASME SF593 Hex Bolt Available in length Ranging From 12 - 1200MM , Check Specification
ASTM F593 Bolts Sizes
- Imperial Sizes: 1/4" - 1-1/2"
- Metric Size: M10-M100
- Length: 12 - 1200MM
Benefits
- Durability, Longevity
- High Tensile Strength
- Corrosion Resistance
- Versatility
Certification
- MTC as per EN 10204 / 3.1B
- 100% Radiography Test Report
- Raw Materials Certificate
- Compliance Certificates
Threads Types
- METRIC
- BSF, UNC
- BSW
- UNF
Head Types
- Hex, Square
- Round,Flat
- Hex flange
- T-head & Triangular
Finishing
- Anodizing, plated zinc-nickel, nickel plated
- Zinc , black oxide, BZP
- Geometry, Dacroment, Hot Dip Galvanised (HDG),
Applications
- Marine Industry
- Chemical Processing
- Food and Beverage
- Power Generation
Packaging Methods
- Corrugated Box
- Pallet
- Small Pack
- Carton
Testing Methods
- Hardness Testing
- Corrosion Testing
- Tensile Testing
- Impact Testing
Neck type
- Oval
- Triangular
- Hex, Square
- Knurled
Production process
- Machining and CNC
- Cold Forging
- Hot Forging
- Customized
Surface Coating
- Cadmium, Galvanized
- Black Oxide
- Teflon, Xylan, Zinc
- Others Upon Request
Cutting Methods
- Hacksaw
- Threaded Rod Cutter
- Angle Grinder
Disadvantages
- Strength Limitations
- Work Hardening
- Galvanic Corrosion
Documentation
- Fumigation Certificates
- Guarantee Letter
- Raw Material Test Reports
ASTM F593 Bolts Supplier in India offers a wide range of commonly used fasteners types
ASTM F593 J-Bolts
ASME SF593 U-Bolts
ASTM F593 Hex Head Bolt
F593 Square Head Bolts
SF593 Shoulder Bolts
ASTM F593 Eye Bolts
ASTM F593 Type 304 Heavy Hex Bolt
F593 Flange Bolts
View Equivalent Grades & Size Chart of ASTM F593 Hex Head Bolt
| NOMINAL SIZE (D) | BODY DIA | HEAD THICK F593 | ASTM F593 THE FLATS | ACROASTM F593 CORNERS | ||||
|---|---|---|---|---|---|---|---|---|
| D (MIN) | D (MAX) | H (MIN) | H (MAX) | F (MIN) | F (MAX) | C (MIN) | C (MAX) | |
| m10 | 9.78 | 10.00 | 6.17 | 6.63 | 15.73 | 17.00 | 17.77 | 18.48 |
| m20 | 19.67 | 20.00 | 12.12 | 12.88 | 29.16 | 30.00 | 32.95 | 34.64 |
| m12 | 11.73 | 12.00 | 4.24 | 7.76 | 17.73 | 19.00 | 20.03 | 20.78 |
| m16 | 15.73 | 16.00 | 9.68 | 10.32 | 23.67 | 24.00 | 26.75 | 27.71 |
| m24 | 23.67 | 24.00 | 14.56 | 15.44 | 35.00 | 36.00 | 39.55 | 41.57 |
| m48 | 47.38 | 48.00 | 28.93 | 31.07 | 72.60 | 75.00 | 82.76 | 86.60 |
| m36 | 35.61 | 36.00 | 21.63 | 23.38 | 53.80 | 55.00 | 60.79 | 63.51 |
| m42 | 41.38 | 42.00 | 25.03 | 26.97 | 62.90 | 65.00 | 71.71 | 75.06 |
| m56 | 55.26 | 56.00 | 33.80 | 36.2 | 82.20 | 85.00 | 93.71 | 98.15 |
| m80 | 79.26 | 80.00 | 48.42 | 51.58 | 111.00 | 115.00 | 126.54 | 132.72 |
| m64 | 63.26 | 64.00 | 38.68 | 41.32 | 91.80 | 95.00 | 104.65 | 109.70 |
| m72 | 71.26 | 72.00 | 43.55 | 46.45 | 101.40 | 105.00 | 115.60 | 121.24 |
| m90 | 89.13 | 90.00 | 54.26 | 57.74 | 125.50 | 130.00 | 143.07 | 150.11 |
| m100 | 99.13 | 90.00 | 60.10 | 63.9 | 140.00 | 145.00 | 159.60 | 167.43 |
| Diameter (D) | Body Diameter (D) | Across the Flats (F) | Across the Corners © | Head Height (H) | Thread Lengths (T) | |||||
|---|---|---|---|---|---|---|---|---|---|---|
| MAX | MIN | MAX | MIN | MAX | MIN | MAX | MIN | < 6” | > 6” | |
| 1/2 | 0.515 | 0.482 | 0.875 | 0.85 | 1.01 | 0.969 | 0.364 | 0.302 | 1.25 | 1.5 |
| 5/8 | 0.642 | 0.605 | 1.062 | 1.031 | 1.227 | 1.175 | 0.444 | 0.378 | 1.5 | 1.75 |
| 3/4 | 0.768 | 0.729 | 1.25 | 1.212 | 1.443 | 1.383 | 0.524 | 0.455 | 1.75 | 2 |
| 7/8 | 0.895 | 0.852 | 1.438 | 1.394 | 1.66 | 1.589 | 0.604 | 0.531 | 2 | 2.25 |
| 1 | 1.022 | 0.976 | 1.625 | 1.575 | 1.876 | 1.796 | 0.7 | 0.591 | 2.25 | 2.5 |
| 1 1/8 | 1.149 | 1.098 | 1.812 | 1.756 | 2.093 | 2.002 | 0.78 | 0.658 | 2.5 | 2.75 |
| 1 1/4 | 1.277 | 1.223 | 2 | 1.938 | 2.309 | 2.209 | 0.876 | 0.749 | 2.75 | 3 |
| 1 3/8 | 1.404 | 1.345 | 2.188 | 2.119 | 2.526 | 2.416 | 0.94 | 0.81 | 3 | 3.25 |
| 1 1/2 | 1.531 | 1.47 | 2.375 | 2.3 | 2.742 | 2.622 | 1.036 | 0.902 | 3.25 | 3.5 |
| 1 3/4 | 1.785 | 1.716 | 2.75 | 2.662 | 3.175 | 3.035 | 1.196 | 1.054 | 3.75 | 4 |
| 2 | 2.039 | 1.964 | 3.125 | 3.025 | 3.608 | 3.449 | 1.388 | 1.175 | 4.25 | 4.5 |
| 2 1/4 | 2.305 | 2.214 | 3.5 | 3.388 | 4.041 | 3.862 | 1.548 | 1.327 | 4.75 | 5 |
| 2 1/2 | 2.559 | 2.461 | 3.875 | 3.75 | 4.474 | 4.275 | 1.708 | 1.479 | 5.25 | 5.5 |
| 2 3/4 | 2.827 | 2.711 | 4.25 | 4.112 | 4.907 | 4.688 | 1.869 | 1.632 | 5.75 | 6 |
| 3 | 3.081 | 2.961 | 4.625 | 4.475 | 5.34 | 5.102 | 2.06 | 1.815 | 6.25 | 6.5 |
Get ASTM F593 Type 316 Threaded Rod & F593C Hex Bolts With High Tensile Strength, Check Mechanical Properties
| Property | Grade 1 (304 SS) | Grade 2 (304L SS) | Grade 3 (316 SS) | Grade 4 (Higher Strength) |
|---|---|---|---|---|
| Tensile Strength | Minimum 70 ksi (485 MPa) | Minimum 70 ksi (485 MPa) | Minimum 70 ksi (485 MPa) | Minimum 75 ksi (515 MPa) |
| Yield Strength | Minimum 30 ksi (205 MPa) | Minimum 30 ksi (205 MPa) | Minimum 30 ksi (205 MPa) | Minimum 40 ksi (275 MPa) |
| Elongation | Minimum 30% in 2" (50.8 mm) | Minimum 30% in 2" (50.8 mm) | Minimum 30% in 2" (50.8 mm) | Minimum 25% in 2" (50.8 mm) |
| Hardness | Maximum 92 HRB | Maximum 92 HRB | Maximum 92 HRB | Maximum 92 HRB |
| Size (inches) | Grade 1 | Grade 2 | Grade 3 | Grade 4 | Grade 5 | Grade 6 |
|---|---|---|---|---|---|---|
| 1/4" | 3.2 | 4.3 | 5.6 | 6.4 | 7.6 | 8.8 |
| 5/16" | 7.1 | 9.4 | 12.1 | 14.3 | 17.0 | 19.6 |
| 3/8" | 11.4 | 15.0 | 19.1 | 22.3 | 26.3 | 30.5 |
| 7/16" | 17.6 | 22.9 | 28.2 | 33.2 | 39.2 | 45.4 |
| 1/2" | 25.1 | 33.1 | 41.9 | 49.4 | 58.3 | 67.6 |
| 5/8" | 44.2 | 57.4 | 72.4 | 85.5 | 101.6 | 118.5 |
| 3/4" | 77.2 | 100.5 | 127.5 | 151.5 | 178.6 | 208.6 |
| 7/8" | 115.3 | 150.5 | 191.3 | 227.1 | 267.3 | 310.5 |
| 1" | 165.7 | 216.5 | 274.6 | 328.9 | 389.4 | 457.4 |
| Property | Value |
|---|---|
| Density | 7.75 to 8.05 g/cm³ |
| Thermal Conductivity | 16.2 W/m·K |
| Coefficient of Thermal Expansion | 16.0 × 10⁻⁶ /°C |
| Melting Range | 1,140°C to 1,145°C |
| Hardness | 70-90 HRB |
Get F593 Stud Bolt & ASTM F593 Type 304 Bolt With High in Chromium Environment, Check Chemical Composition.
| Element, max except as shown | Alloy Group 1, Type 304 | Alloy Group 2, Type 316 |
|---|---|---|
| Carbon | 0.08% | 0.08% |
| Manganese | 2.00% | 2.00% |
| Phosphorus | 0.045% | 0.045% |
| Sulfur | 0.030% | 0.030% |
| Silicon | 1.00% | 1.00% |
| Chromium | 18.0 to 20.0% | 16.0 to 18.0% |
| Nickel | 8.0 to 10.5% | 10.0 to 14.0% |
| Copper | 1.00% | |
| Molybdenum | 2.00 to 3.00% |
| Bolt Size (Diameter) | Thread Count (Threads per Inch) | Weight per 100 Bolts (lbs) | Weight per 100 Bolts (kg) |
|---|---|---|---|
| 1/4" (0.250") | 20 | 0.6 | 0.27 |
| 5/16" (0.3125") | 18 | 1.0 | 0.45 |
| 3/8" (0.375") | 16 | 1.5 | 0.68 |
| 7/16" (0.4375") | 14 | 2.0 | 0.91 |
| 1/2" (0.500") | 13 | 2.6 | 1.18 |
| 5/8" (0.625") | 11 | 4.0 | 1.81 |
| 3/4" (0.750") | 10 | 6.0 | 2.72 |
| 7/8" (0.875") | 9 | 8.5 | 3.86 |
| 1" (1.000") | 8 | 11.0 | 4.99 |
| Alloy Group | Alloy Designation | Alloy Type |
|---|---|---|
| 1 | 303, 304, 304L, 305, 384, XM1, 18-9LW, 302HQ, 303Se | Austenitic |
| 2 | 316, 316L | Austenitic |
| 3 | 321, 347 | Austenitic |
| 4 | 430, 430F | Ferritic |
| 5 | 410, 416, 416Se | Martensitic |
| 6 | 431 | Martensitic |
| 7 | 630 (17-4) | Precipitation Hardening |
| Country Name | Delivery Time |
|---|---|
| Turkey | |
| UAE | |
| Malaysia | |
| Oman | |
| Saudi Arabia | |
| Singapore | |
| Egypt | |
| Jordan | |
| South Africa |
| Aspect | ASTM F593 Bolts | ASTM A193 Bolts |
|---|---|---|
| Material | Stainless steel (e.g., SS 304, SS 316) | Alloy and stainless steels (e.g., SS, Inconel) |
| Applications | General-purpose, corrosion-resistant | High-temp, high-pressure (e.g., power plants) |
| Temp Range | Up to ~925°C (1700°F) | High-temp service, up to ~1100°C (2000°F) |
| Strength | Moderate strength | High strength, especially at elevated temps |
| Bolts & Fasteners | Bolts, hex cap screws, studs | Primarily bolts, for high-stress applications |
| Temperature Range | Performance |
|---|---|
| High Temps | -Max temp: 870°C (1600°F) , 925°C (1700°F) . -Good strength |
| Low Temps | Performs well |
| Thermal Expansion | contracts with temp changes. |
| Alternative Materials | For >900°C (1650°F) |
| Property |
|---|
| Weldability |
| Welding Methods |
| Heat Control |
| Post-Weld Treatment |
| Impact on Strength |
| Corrosion Resistance |
| Reasons for Welding |